Energy transfer from Cr3+ to Nd3+ and NIR luminescence of Nd3+ in lead borate glasses
lead borate glasses Cr3+ and Nd3+ ions
2011/5/5
Energy transfer processes from Cr3+ to Nd3+ and NIR luminescence of Nd3+ ions at 1.06 μm in Cr–Nd co-doped lead borate glasses have been investigated. The spectroscopic investigation indicates that Cr...
Borate glasses with PbO and PbCl2 containing Dy3+ ions
glasses dysprosium ions optical properties
2011/5/6
Oxychloroborate glasses containing Dy3+ ions in the B2O3–PbCl2–PbO–Al2O3–WO3 system
were studied using X-ray diffraction, Raman, FT-IR, absorption, excitation and luminescence
spectroscopy. The resu...
Influence of PbX2 (X = F, Cl, Br) content and thermal treatment on structure and optical properties of lead borate glasses doped with rare earth ions
lead borate glasses rare earth ions thermal treatment luminescence, up-conversion
2011/5/6
Oxyhalide lead borate glasses doped with rare earth ions have been studied before and after thermal
treatment. The rare earths as optically active ions were limited to the Er3+ ions. Near-infrared
l...
Near-infrared luminescence of rare earth ions in oxyfluoride lead borate glasses and transparent glass-ceramic materials
oxyfluoride glasses transparent glass-ceramics
2011/5/5
Oxyfluoride lead borate glasses singly doped with Nd3+ and Er3+ ions have been studied before and after thermal treatment. The orthorhombic PbF2 crystallites are formed during thermal treatment, which...
Energy transfer from Cr3+ to Nd3+ and NIR luminescence of Nd3+ in lead borate glasses
lead borate glasses Cr3+ and Nd3+ ions
2011/5/5
Energy transfer processes from Cr3+ to Nd3+ and NIR luminescence of Nd3+ ions at 1.06 μm in Cr–Nd co-doped lead borate glasses have been investigated. The spectroscopic investigation indicates that Cr...
Energy transfer from Yb to X (X = Tm, Er) in lead borate glasses
lead borate glasses rare earth ions energy transfer process up-conversion emission
2011/4/28
Energy transfer processes in lead borate glasses doubly doped with Yb–Tm and Yb–Er have been investigated at room temperature under excitation of Yb at 975 nm. The non-resonant energy transfer from 2F...